ASTM A213 T11 Màndarga Tuyo

Tegtal produit bi

ASTM A213 Grade T11 tub ferritik la bu amul benn ñaw, ñu koy jëfandikoo ci vapër bu tàng ak ci gaz buy génn. Grade bi dañu ko tëral ngir komposant yi yor pression ci biir chaudière yu am doole, HRSG, chauffage petrochimique ak weccoo tàngoor yu am tàngoor wu kawe, fu acier carbone mënul tëye resistance oxidation wala doole creep.
Octal Pipe dafay joxe T11 ci anam wu jaar yoon, ak seytu dimension, test bu mat sëkk ci ASTM A213/A1016 ak sertifikaa moulin, suko defee mu mëna dem ci chaudière bi ak defarum liggéey bi.

astm a213 t11 tubing bundles for boiler and superheater service - octal pipe

Composition chimique

Këf	Mbinde (%)	Dóor ndam
C	0.05 – 0.15	Dafay joxe doole ak baña raam, mën nañu ko souder
Mn	0.30 – 0.60	Ductilité, liggéey bu tàng
Si	0.50 – 1.00	Dafay jàppale baña oxidation
P	Lu néew wala lu tollu ci 0.025	Dafay tënk fragilité
S	Lu néew wala lu tollu ci 0.025	Kontrole ngir dëgër
Cr	1.00 – 1.50	Resistance à l'escalier ci vapër / gaz de combustion
Mo	0.44 – 0.65	Dooley raam ak rupture

Balance chromium–molybdenum bi dafa gëna suufe T22 wala yeneen grade Cr yu gëna kawe, moo tax T11 dafay gëna yomba bënn ak souder, waaye mingi wéy di dundu 500–600 degre.

Màndarga mekanik

Moom mu ngi	Wareef	Yitté
Force à traction	Lu ëpp wala lu tollu ci 415 MPa (60 ksi)	Kàttan sargal
Dooley génne (0.2%)	Lu ëpp wala lu tollu ci 205 MPa (30 ksi)	Dafay tere deformaasioŋ budul jeex
Guddaay	Lu ëpp wala lu tollu ci 30%	Dañu ko soxla ngir bënn, bobi, soudure
Dëgër	Lu néew wala lu tollu ci 163 HBW	Dafay wéy di dëgër ngir dawal welo termik

Valeur yii méngoo nañu ak anam yi ñuy jaar ba mëna joxe -ak-tempered, maanaam projet yu am doole ak raffinerie yi dañuy faral di leeral.

Defar ak pajum tàngoor

Ci wàllu serwiis tube chaudière, yoon wi dafa am solo ni chimie bi. Tuyo Octal dafay jëfandikoo yoon wu jaar yoon ci wàllu ASTM A213/A1016:

alloy billet dafay tàng - ñu bënn ko wala ñu génne ko ngir sos benn son bu lëmu
Tube bi dafa tàng-rule wala sedd-ñu tëye ko ci OD biñ santaane, miir bi ak kaw gi (dafa am solo ci tube yiy weccoo tàngoor)
Tube bi dañu koy normalise ci lu tollu ci 940–980 degre ngir setal matrix ferritic bi, dindi band yi ak méngale màndarga mekanik yi ci guddaay bi
tube bi deñukoy tempere ci lu tollu ci 675-755 degre ngir defaraat ductilité bi ak tëjug tasaaroo bu baax ci carbure yi ci barab bi

N+T cycle bi moo jox T11 microstructure bu dëgër: chromium mën na defar filmu oxide bu dëgër, molybdenum mën na def liggéeyam ci dëgëral creep, te tube bi du gëna dëgër ngir souder. Ginaaw ñu defee ko ci tàngoor, dañuy jubbanti tube yi, natt leen ci anam wu hydrostatique, ba noppi ñu saytu leen ci anam wi ñu ko santaane ci NDE (eddy - courant wala ultrasonic) balaa ñu leen di màrke ak ëmb. Jéego bu nekk dañu koy bind suko defee ñu mëna topp tube bi ci tàngoor wi.

Dimension

Parametre	Range / leeral
Diametru biti	12,7 ba 127 mm (0,5 ba 5 puus)
Muur bu yaatu	1,2 – 12 mm
Gudd	Lu ëpp 12 m; SRL / DRL / dagg-ci-guddaay
Jeexal jeexal	Plain, biselé, ou preparé pour U-cour / fin
muñ OD	± 1% (ci ASTM A1016 bu nekk)
Toleransu muur	± 10%
Jub	Dafay gëna néew wala tollu ci 0.8 mm/m

Loolu dafay muur tube panneau chaudière yiñ gëna xam, serpentin superchauffage/rechauffage, ak serpentin chauffage raffinerie.

Liggéeyu serwiis

Ci liggéey bi T11 dafay forme oxide bu bari chromium, kon ñàkka am wen ci tube bi ak tabax scale bi dañu gëna néew luñu koy méngale ak acier carbone. Molybdenum dafay yeexal creep ak rupture, te loolu lu am solo la ci tube yiy toog ci biir tàngoor ak pressure ay junni waxtu. Ndax liñu defaree ferrite la, tube bi mën na muñ cycle tàmbali-dakkal ci HRSGs ak usine cogeneration te du gaawa ñàkk njub. Soudure yi dañuy wéy di am njub ginaaw PWHT sudee ñu jëfandikoo metal filler bu woyof.

Aplikaasioŋ yi

waterwall chaudière, superchauffage, réchauffage et tubes d'économiseur dans les centrales thermiques
HRSG / defarkatu vapër yuñ boole -
chauffage petrochimique ak raffinerie
-cock tamperatiir bu kawe-ak-tube weccoo tàngoor
utilite bu tàng ak ligne de processus ci biir kuuraŋ ak chimik

Saytu ak joxe këyit

Test bi ñu ngi koy def ci anam wu méngoo ak ASTM A213 ak sàrti A1016. Lu ci melni saytu hydrostatic wala courant eddy ngir xam ndax kuur bi dëgër na, saytu tension ak dëgëraay ci lot traitement bu nekk, plateau/flaring ngir firndeel ductilité, boole ci saytu gis-gis ak dimension. Ngir projet yi am QA/QC bu gëna kawe, Octal Pipe mën na yokk ay saytu ultrason wala radiografi. Tube yépp ñu ngi leen jox EN 10204 3.1 wala 3.2 MTCs suko defee boroom bi mëna joxe resultaa chimik, mekanik ak NDE ci nimero tàngoor.

Lu tax nga jël ASTM A213 T11 ci tuyo octal

Tube Cr{0}}Mo sans couture réel dans un état normalisé - et -tempéré, non seulement tube en acier de carbon
Dimension yi, test yi ak màrk yi méngoo ak doole, chaudière, HRSG ak leeral yi ci raffinerie
export-paket yuñ defaree aar ngir yobbu lu sori-
jàppale ingenieur ngir méngale T11 ak grade Cr-Mo (T22, A335 P11/P22) sudee benn jumtukaay bi dafay jëfandikoo aleage yu bari
xëyma xët bind produit - njëkk ak xarala yu leer, ngir jàppale sa sit bu bees mu indexe ni xëtu furnisër, nekkul ëmbiitu template

laaj ak tontu